Plures clavem puncta de Welding deformatio et adolebitque-per CCCIV Aliquam ferro laminam

Maxime difficile problema estCCCIV immaculatam ferro laminamWelding est welding penetratio et deformatio. InCCCIV immaculatam ferro laminamhabet parvum gradum exhibere. Hoc est subiecta loci calefactio et refrigerationem in welding processus? Eam format inaequaliter calefacit et refrigerationem, et weldment et producendum inaequalis accentus. Et contentionem, cum longitudinalis breviare de Weld excedit quadam valorem in ore tenuis laminam, quod mos producere magis gravi fluctus, sicut deformatio? Eam mos afficiunt figura species in workpiece.
Et pelagus mensuras superiores solvere ardeat, per et deformationem CCCIV immaculatam ferro laminam durante welding sunt ut sequitur:

I. Stricte control calor initus in Welding iuncturam, eligere oportet quodammodo welding modum et processum parametri (maxime welding current, arcus intentione, welding celeritate).

II. Fere, minor nozzles sunt plerumque propter welding CCCIV immaculatam ferro laminis, sed commendamus usura maior COLLENTIA Diametris quantum fieri potest, ita ut weld tempus, et in aere potest esse in longiore, ut possit formari potest esse in aere, ut possit effici potest esse bonum antioxidant potest esse, ut possit esse in animo potest esse, ut non potest esse bonum antioxidante

3. When using φ1.5 cerium tungsten rod, the sharpness of the grinding should be sharper, and the length of the tungsten rod protruding from the nozzle should be as long as possible, which will make the base metal melt faster, that is to say, the melting temperature The rise is faster, the temperature will be more concentrated, so that we can melt the position that needs to be melted as fast as possible, and will not let the temperature of more Matrix oriri, ut area ubi internum accentus de materia mutat minorem, et eventually deformatio materialis etiam reduci.

IV. Conventus mole sit accurate et interface Gap sit ut parvum fieri potest. Si gap leviter maior est facile uri per vel formare maius weld gibba.

V. Hardcover fixtures debet esse? Et clamping vim sit libratum et etiam. The key point of welding stainless steel sheet is to strictly control the line energy on the welding joint, and try to reduce the heat input as much as possible under the premise that the welding can be completed, so as to reduce the heat-affected zone and avoid the occurrence of the above defects.

VI. Eligens rationabile Welding serie praecipue momenti ad moderantum in RELICTUM deformatio welding. Nam structuram symmetriorum welds, symmetrical welding debet esse quantum fieri potest; latus. Deformatio tergo Welding sufficit eliminare deformatio fronte parte ut altiore deformatio reducitur.

VII. Optimum est CCCIV immaculatam ferro laminam laser Welding, 0.1mm potest esse conflatis et laser macula magnitudinem potest esse adaequatum libidinis, quod potest esse bene. Non est deformatio Ratio omnino.